衝撃強度が, 一般窯業製品, 特に食器類に就て, 重大な性質の一なることは云ふ迄も無い。日常の取扱ひに際して起る破壞は多くの場合殆んど此の撃衝力の作用に原因するものである。勿論食器類の衝撃強度は, 其の周邊及底の厚味に關係するのであるが, 衝撃強度が, 其の形態にも亦大いに影響されるものなることを忘れてはならぬ。
本報告では先づ, 我國に於て製造された皿類の内蒐集し得たものに就て, 通常此の方面に用ひられゐる振子式衝撃試驗機により, 其等が大體如何程の強度を有つものなるやを試驗したのである。共の結果周邊と底とのなす角, 云ひ換へれば, 此の試驗の場合撃衝力の方向と周邊とのなす角が, 衝撃強度に對して相當重大な關係を有つてゐると云ふ事を, 事實として知り得たのである。然し乍ら其の嚴密な數字的關係は, 其の目的の爲に特に製作した試驗體を用ひて, 更に完全な試驗をした結果によらねば知り得ないのである, 本試驗は我國に於ける製品の衝撃強度の大體を得たに過ぎない。

抄録全体を表示

In the soda-lime-iron oxide-silica glasses whose general glass composition is 72%SiO₂, (12-x)% CaO, x% Fe₂O₃, 16% Na₂O, the source of iron oxide has been used ferrous oxalate, gradually changing the value of the x from 0 to 12 one by one. In such case a study has been made as to the state of oxidation of the iron oxide, and of glass color as well as transmission curves and at same time made a comparison of these changes with FA-series described in the 3rd report.
(A) An amount of FeO contained in the glass and an amount of total iron oxide as Fe₂O₃ have been obtained through analysis and the percentage ratio of FeO/FeO+Fe₂O₃ has been sought there from, which being as follows: -
From this result it has been found that the percentage ratio of the FeO/FeO+Fe₂O₃ in all glasses except FD-1 and FD-2 will be greater as amounts of iron oxide go to increase but this tendency will cease at a certain limit, whence it will gradually approach a definite value. Next comparing the said percentage ratio of FeO/FeO+Fe₂O₃ with that of FA-series it has been noted that in this FD-series it will be increased as the iron content increases while in FA-series it will be contrary to the former.
As to the colors, glasses having smaller iron content are bluish and the amounts of Fe and Fe₂O₃ increase with the increase of iron content, presenting greenish blue glasses. When the iron content is considerably increased it presents dark green color. Compared with glasses in FD-series the color of FA-series glasses are yellowish, and a comparison has been made between glasses having the same amount of iron content in both series and, in general, glasses in FD-series are deeper and darker than those in FA-series, with respect to the colors.
(B) The transmission curves have been measured. It has been found that the transmission will be smaller as iron oxide content increases. The transmission curves of glasses in the FD-series have been compared with those of the glasses corresponding to glasses in FA-series. The maximum transmission range of glasses in FD-series has been found in the side where wave length is shorter and considerably lower.
Furthermore, a comparison has been made as to the limit of wave length which transmit the glass, between glasses of both FA and FD-series. It has been known that among the glasses having smaller iron contents there is substantially no difference therebetween.
However, as the iron content increases a difference will gradually arise between the two and glasses in FD-series transmit wave length shorter than that transmitted by FA-series glasses.
As to the transmission in 700mμ the glasses in FD-series are lower than those in FA-series and the lowering degree is for greater than the difference in the visible range.

抄録全体を表示

混合セメントに關する著者の多數の研究殊に多珪酸質白土を30-50%混用した多珪酸型混合セメント及び其の凝結を促進するために石灰を適當に加へた石灰珪酸混合セメント等に於て既報の研究を繼續して行つた結果を茲に報告したので次の其の要點を摘録しやう。
(1) 第14報迄に掲げた各種の混合セメントの強度試驗は多くは4週迄の強度であつたから茲には夫れ以後8週, 13週, 26週, 52週 (1年) 等の長期硬化の強度を硬練1:3-モルタル及び軟練1:1:2-モルタルに就て比較試驗した結果を示し硬練では各種混合セメントに4週以後は例外なく普通ポルトランドセメントより優良で26-52週の強度は50-70%以上増大し尚強度の増進を止めないがら2年, 3年等の長期強度は更に優秀となる。他方軟練モルタルの強度に於ては混合セメントの短期強度は劣るが13-26週位からポルトランドセメントに肉薄し其の後は之を凌駕して來るから土木用コンクリートに最も適するセメントが得られる。
(2) 是等のセメントの中遊離石灰4-6%を殘存するクリンカーから得た普通ポルトランドセメントは極めて不安定であるのに對し之に頁岩灰, 可溶性珪酸白土等を適當に加へることに依つて完全に安定なセメントが得られることは混合セメントの特徴の一と考へられる。
(3) 從つて此の方法を延長して最初から遊離石灰を5-10%の樣に多量に含有するクリンカーを作り之に適當量の多珪酸質白土を混用することに依つて此のクリンカーだけでは到底セメントにならぬものから完全に安定で而も短期強度が高く凝結の遲くない混合セメントを得ることが出來る。之は別報したクリンカーに加ふるに白土と石灰石とを混じて豫め900℃に〓燒して白土を乾燥し石灰石を石灰にした混合材を以つてした特殊の石灰珪酸混合セメント (特許出願公告中) と同一趣旨のもので其の追加特許として出願中である。
終に此の研究にはハルピンセメント株式會社の補助を受け研究者松岡及び能味は他の各種の研究と共に相次いで會社より教室に派遣されたものである。茲に厚く感謝の意を表したい。

抄録全体を表示