  • 山陽パルプ株式会社
    1968 年 22 巻 12 号 p. 47-54
    発行日: 1968/12/01
    公開日: 2009/11/10
    ジャーナル フリー
  • 内藤
    1968 年 22 巻 12 号 p. 57-59
    発行日: 1968/12/01
    公開日: 2009/11/10
    ジャーナル フリー
  • 北野 昭俊
    1968 年 22 巻 12 号 p. 591-598
    発行日: 1968/12/01
    公開日: 2010/01/22
    ジャーナル フリー
  • 三宅 基夫
    1968 年 22 巻 12 号 p. 600-610
    発行日: 1968/12/01
    公開日: 2009/11/10
    ジャーナル フリー
    Wood characteristices and kraft pulp properties from eleven kinds of hardwood grown in Hokkaido were examined, and then the correlation between the properties of woods and their pulps were studied.
    The results were as followes :
    1) Specific gravity of woods correlated with lignin content (+) * and holocellulose content (-), and besides correlated with fiber width (-), lumen width (-), and the ratio of fiber width to lumen width (-).
    2) Pentsan and α-cellulose content in pulp were correlated with their content in wood (+) respectively, therefore the chemical properties of pulp may be inferred by the results of chemical analysis of wood.
    3) The yield of pulp was strongly correlated with α-cellulose content in the wood (+).
    4) Important factors affecting on the breaking length and burst strength of pulp-sheet were the fiber length (+) and the ratio of fiber width to lumen width (+), and the former was slightly more importand than the latter. Also the tear strength was most affected by fiber length (+).
    5) Sheet-density was found to be correlated with the ratio of fiber width to lumen width (+) and pentsan content (+). And breaking length and burst strength were primarily correlated with the density (+). But tear strength is most affected by fiber length (+), then the density.
    6) Correlation between 0-span breaking length and pulp-sheet strength was found to be relatively slight.
    * Sign indicates whether relationship is positive (+) or negative (-)
  • III セミケミカルパルプの強度変化
    荻原 允隆, 荒井 健一郎
    1968 年 22 巻 12 号 p. 611-616
    発行日: 1968/12/01
    公開日: 2009/11/10
    ジャーナル フリー
    Unbleached semi-chemical market pulp from coniferous wood (USCP) and bleached one prepared from the former (BSCP) were hydrolyzed with powdered cellulase, and the changes of the strength characteristics of paper sheets as well as some variables assumed to affect the strength were studied. Tensile and tear strength of the pulps decreased with the time of cellulase treatment.
    From the changes of characteristics including that of yield of pulps with the cellulase treatment, water retention value (WRV), fine content, specific volume of web, pentosan content, number-average fiber length and lignin content, the following facts were inferred :
    (1) Changes in tensile strength of BSCP with cellulase treatment were caused by the decrease in interfiber hydrogen bonding and interfiber friction because of the decrease in fiber length, fine content and pentosan content ; the results were similar to those obtained in our previous study made with kraft pulps.
    (2) In spite of the fact that fine content and WRV of USCP increased considerably with cellulase treatment, specific volume of the web increased definitely ; the web became bulky as the lignin content in USCP increased with the cellulase treatment, and the tensile strength decreased.
    (3) Changes in tear strength with cellulase treatment were considered as the results of lowering of fiber length both in USCP and BSCP as well.
  • 遠藤 治郎
    1968 年 22 巻 12 号 p. 617-620
    発行日: 1968/12/01
    公開日: 2009/11/10
    ジャーナル フリー
    パルプ蒸解液, ことに白液のアルカリ成分を, 電位差滴定法によって, 自動分析する検討が行なわれ, その結果, 白液中アルカリ成分の自動分析装置が試作された。この装置によって, 白液は任意に設定された時間間隔で分析され, 滴定曲線から, 各アルカリ成分は容易に算出される。
  • ハイザー エドワード・J, ベーカー ハリー・M
    1968 年 22 巻 12 号 p. 621-627
    発行日: 1968/12/01
    公開日: 2010/05/07
    ジャーナル フリー
  • J. L. Betts, G. G. Wilson
    1968 年 22 巻 12 号 p. 628-634
    発行日: 1968/12/01
    公開日: 2009/11/10
    ジャーナル フリー
    クラフトパルプ工場漂白排水と未晒スクリーン排水を別々にまたは, 特別の工場の三排水中と同じ割合に混合して, 若い大西洋産鮭 (Salmo salar) に対する毒性テストを行なった。
    中性pH条件でテストした塩素化段からの漂白排水成分は, 他の成分よりかなり毒性が強い。
    少量の二酸化硫黄で処理すると, 塩素化段の毒性を大きく軽減できた。塩素化成分を他の成分と混合する前に処理すると, 全排水についての毒性軽減の方が小さいけれどかなりのものであった。
    ある第1段変法 (塩素化) 漂白法からの濾液を実験室で調製し, その毒性もテストした。二酸化塩素と塩素を実際に混合したものを, 第一漂白段の通常塩素の代わりに添加すると, 毒性のずっと低い濾液が得られた。
    多くの他の処理法, その相対的効果について述べる。