かさ密度1000kg・m^-3のオートクレープ処理ケイ酸カルシウム板について, 消石灰と石英 (Ca/Si= 0.8), およびセルロース繊維に二水セッコウをCaSO₄換算で0, 5, 10, および20mass %添加し, 180℃で0-160時間, および140℃で0時間飽和蒸気圧下で水熱処理した場合の化学反応と材料強度への影響について研究した.二水セッコウ無添加の場合の反応過程は, 高Ca/Si比C-S-H+石英→C-S-H→1.1nmトバモライトであった.二水セッコウ添加の場合, 二水セッコウは加熱脱水後, 消石灰, および石英と反応して, ヒドロキシルエレスタダイトが生成し, 強度の上昇は停滞した.その後石英と反応し分解して, トバモライトと無水セッコウが生成し, 組織のち密化により高い強度を発現した.二水セッコウ添加量が0, 5, および10mass %の場合, 長時間の処理でトバモライトからジャイロライトへの分解と同時に組織が粗大化し, 強度は低下した.

抄録全体を表示

Phenol resin-alumina cement composite (PRAC composite) with flexural strength as high as 200 MPa has been developed by Hasegawa et al. from the composition of phenolic resin (resol resin), alcohol soluble polyamide, glycerol and alumina cement. In comparing with MDF (macro-defect-free) cement, this newly developed composite has higher flexural strength and resistivity to water and heat. From mechanism study, we indicated the existence of interaction in the interface area between hydroxyl group in phenol resin and alumina cement.
In this paper, the effect on flexural strength of diphenolic and triphenolic compounds with palafolm added in PRAC composite was studied. Addition of a slight amount of diphenolic compounds, such as resorcinol, or triphenolic compounds, such as pyrogallol or phloroglucinol, raised the flexural strength of the PRAC composite by approximately 33% in comparison with that without addition of di-and triphenolic compounds. From the results of model reaction of AC and pyrogallol or phloroglusinol, it was suggested that hydroxyl group and alumina cement play an important role to enhance the strength of the composite.

抄録全体を表示

Alumina cements were manufactured as experiments from aluminium dross ashes and oyster shells. Aluminium dross ashes were oxidized by burning treatment at 1100°C, and oyster shells dried at 110°C. The mixture of pretreatment aluminium dross ashes and oyster shells were crushed in a grinding mill. Alumina cements were obtained by burning ground mixtures. Mixing ratio of these wastes were designed to be 0.25-4.0 CaO/Al₂O₃ mass per cent, and the burning conditions were set to be 1100-1300°C. Alumina cements were characterized by means of XRD and XRF, and the refractoriness were examined in accordance with JIS R2204. Compressive strength of hardened mortar was examined in accordance with JIS R2521.
The results obtained from the present study are as follows.
1) Main components of alumina cements were CA, MA, and C₂AS. The formation of CA was confirmed by burning at 1100-1300°C and set to be 0.43-0.67 CaO/Al₂O₃ mass per cent.
2) Compressive strength of hardened mortar reached at 51.4 N·mm^-2 in 28 days. The refractoriness of alumina cement reached at roughly 1500°C. There seems to be a chance that alumina cement can be used for refractory brick, unreinforced concrete and so on.

抄録全体を表示

From the viewpoint of resource-and energy-saving, and for the purpose of global environmental safeguard, the authors are studying applications of ground granulated blast-furnace slag as a concrete aggregate by paying particular attention to the granulated blast-furnace slag, which is subsidiary produced as an industrial by-product in such a great quantity as 16 million tons a year in Japan.
In order to realize practical use of the ground granulated blast-furnace slag for high strength and durability concrete on the basis of the experimental results in the laboratory, including those which have been reported in the past, the authors compiled in this article experimental research results about applications of the ground granulated blast-furnace slag to the concrete mixed up in a ready-mixed concrete plant qualified by the JIS.
As a result, it was practically clarified that the ground granulated blast-furnace slag can be sufficiently utilized as the aggregate for the high strength and durability concrete.

抄録全体を表示

Permeability properties of incineration ashes suspension due to ceramic membrane in supersonic flow field were investigated.
The permeation flux of coloidal suspension in supersonic flow field decreased by prompt fouling. In filtration for one day, the flux decreased with increasing time because of the pore narrowing.
The membrane resistance increased with increasing time. However, backwashing to take off plugging by nitorogen gas was found to be effective for the recovery of flux.
The permeation flux of coloidal suspension under supersonic flow field decreased with increasing the concentration of slurry. The permeation flux, however, change very little with the concentration for not less than 4 mass%. The limitations of concentration to be fluidized slurry under this experimental conditions was found to be 3.5 mass%.

抄録全体を表示

In recent years, amount of urban waste is increasing and a shortage of land disposal site has been caused as a serious problem. The study was carried out to establish recycling process of fly ash included with chloride without generating any secondary waste. The following summarized the results.
Chloride in the fly ash was leached with water. We can downsize facilities for subsequent process, because volume of residue was reduced by 1/5 to 1/10.
Copper and zinc ions in the residue were leached with sulfuric acid solution. From this filtrate, copper metal was recovered by cementation and zinc hydroxide was recovered by adjustment pH, respectively.
Lead ion was leached with aqueous solution of sodium hydroxide and was recovered as lead sulfide. At the same time, calcium sulfate was converted to calcium hydroxide which was able to be utilized as a raw material for cement.
The waste water caused from this process could be content with effluent standard by water treatment attaching importance to de-selenium processing.

抄録全体を表示