  • 田上 道弘, 小田嶋 隆, 宇佐美 正
    鋳物
    1988年 60 巻 8 号 518-523
    発行日: 1988/08/25
    公開日: 2011/09/08
    ジャーナル フリー
      Effects of heat treatment and copper contents on the fatigue strength of high aluminum zinc alloys cast into metallic mold were investigated using a uni-bending fatigue machine at the rotating speed of 1,800 rpm. Zn-28.2%Al-1.1%Cu-0.02%Mg alloy has the highest fatigue strength (13.5kgf/mm2) at 107 cycles among the as-cast alloy castings tested. Addition of 9.4%Cu does not improve the fatigue strength of as-cast Zn-11.8%Al-1.0%Cu-0.02%Mg alloy. Heat treatment at 360 degC for 20h followed by air cooling results in about 20% improvement of fatigue strength of as-cast Zn-22.2%Al and Zn-28.2%Al-1.1%Cu-0.02%Mg alloys. However, heat treament at 360 degC for 20h followed by water quenching causes a decrease in fatigue strength by 30% of as-cast Zn-22.2%Al-alloys, resulting in the minimum fatigue strength among the alloys studied.
  • 久保田 耕平, 佐藤 勉, 二宮 隆二, 星谷 光治
    鋳物
    1995年 67 巻 5 号 331-335
    発行日: 1995/05/25
    公開日: 2011/06/11
    ジャーナル フリー
      The uniaxial type and plane bending type fatigue tests of Zn alloys were performed. Eleven alloys were tested. They included existing alloys such as ZAS (Zn-4 Al-3 Cu), ZA alloys such as ZA 27 (Zn-27 Al-2 Cu), and alloys devloped newly such as Z 1010 (Zn-10 Al-10 Cu). The results were follows. (1) The fatigue strength of 104 cycles improves with the tensile strength of alloys increases. The fatigue strength of Z 1010 in the uniaxial test is 222 MPa, which is 30 % higher than that of ZAS (169 MPa). (2) The fatigue strength of 106∼107 cycles does not depend on the tensile strength of alloys. The fatigue strength of the uniaxial test and the bending test are 130 MPa and 100 MPa respectively, which are settled values. (3) The ratio of the fatigue strength to the tensile strength decreases with the strength of alloys increases.
  • 佐藤 勉, 久保田 耕平, 二宮 隆二
    鋳物
    1993年 65 巻 6 号 457-461
    発行日: 1993/06/25
    公開日: 2011/06/22
    ジャーナル フリー
      Two high strength Zn alloys for molds, Z 1610 (Zn-16 Al-10 Cu-0.02 Mg) and Z 2520(Zn-25 Al-20 Cu-0.02 Mg), are newly developed. The fatigue test and the wear test of these new alloys are carried out to compare with existing alloys, ZAS (Zn-4 Al-3 Cu-0.05 Mg), ZA 12 (Zn-12 Al-1.5 Cu-0.02 Mg) and ZA 27 (Zn-27 Al-2.5 Cu-0.02 Mg). The results are as follows. (1) The low cycle fatigue strengths of Z 1610, Z 2520, ZA 12 and ZA 27 are much higher than ZAS. For example the fatigue strength at 1 × 105 cycle of Z 1610 is 142 MPa while that of ZAS is 123 MPa. (2) The high cycle fatigue strengths of all tested alloys are much the same. That at 1 × 107 cycle is about 100 MPa. (3) Z 1610 and Z 2520 show the better wear property than ZAS, ZA 12 and ZA 27. Z 1610 and Z 2520 are excellent materials for molds.
  • 田上 道弘, 大谷 辰夫, 宇佐美 正
    軽金属
    1988年 38 巻 2 号 107-113
    発行日: 1988/02/29
    公開日: 2008/07/23
    ジャーナル フリー
    Effects of heat treatment, contents of Cu and Mg, and rolling reduction on the damping capacity, tensile strength, hardness and elongation were studied for Zn-22% Al alloys. Damping capacity of the alloys was measured in terms of internal friction using the inverted torsion pendulum method at frequency of 1 to 3Hz in atmosphere. The alloy heat-treated at 360°C for 2hrs followed by water quenching exhibits the highest internal friction (Q-1, 4.5×10-2). Aging at 250°C for 1hr results in about 38% decrease in the value of internal friction. Addition of 0.021%Mg lowers the internal friction of as-cast alloys containing 0.3%Cu by about 50%, whereas addition of 0.3%Cu has little effect on the internal friction of as-cast alloys (Q-1, 1.1×10-2). Addition of 0.3%Cu and 0.3%Cu, 0.021% Mg cause a decrease in internal friction of heat-treated alloy by about 33% and 68%, respectively. Rolling reduction of 80% results in the improvement of internal friction of heat-treated alloy containing 0.3%Cu and 0.008%Mg by 30%. Cu and Mg addition increases the tensile strength and hardness of heat-treated alloys. Simultaneous addition of 0.3%Cu and 0.008%Mg decreases elongation to the range of 1%, while addition of 0.3% Cu has no effect on the elongation of the heat-treated alloys.
  • 有元 健
    スポーツ社会学研究
    2015年 23 巻 2 号 45-60
    発行日: 2015/10/15
    公開日: 2016/10/07
    ジャーナル フリー
     本論は、2020年東京オリンピック・パラリンピック開催を契機として新自由主義的な国策と都市形成が結びつきヘゲモニーを構築するあり方を、東京大会招致から決定後の諸言説・表象を素材として分析し批判するものである。本論はまず、「今、ニッポンにはこの夢の力が必要だ。」という招致スローガン及びポスターを記号論的に分析する。そこでは領土的な意味合いを視覚的に連想させる「日本」ではなく音声化された「ニッポン」という記号が用いられることによって情緒的なナショナリズムが喚起されると同時に、東京という個別的な都市が「ニッポン」に置き換えられることによって、個別の利益が全体の利益を代表=表象するというヘゲモニー構造が自然化される。本論は次に、東京大会開催決定後のエコノミストや都市政策専門家の新自由主義的言説の中で2020年東京大会がグローバル・シティとしての東京の都市開発戦略にどのように奪用されているかを分析する。そこではオリンピック開催を契機とした都市開発をめぐるユーフォリアがたきつけられながら、アベノミクスの経済政策と東京一極集中化が肯定されていく。だがそうした都市開発や経済政策の受益者は階級的に選択されたものとなる。本論は最後に、そこで語られるオリンピック・パラリンピック開催の「夢の力」が、現実にはどのような結果を導きうるのかを2012年ロンドン大会の事例を参照しながら批判的に捉えていく。レガシー公約とは反対に、ロンドン大会が生み出した都市のジェントリフィケーションは貧困層を圧迫し、またスポーツ普及は全体として進まず、参加者の階級的格差が広がっている。「夢の力」を当然のように期待し、それが良きものだと前提することは、オリンピック・パラリンピックというスポーツ文化を奪用しようとする限られた一部の特権的な受益者を批判する視点を失うことになる。