2011 Volume 65 Issue 1 Pages 184-189
Aiming at reducing environmental burdens such as greenhouse gas emission, protland blast-furnace slag cement partially replaced with limestone powder, at slag content of 40 percent, was studied. When the base cement was replaced with a limestone powder, with a fineness of 3,500 and 5,480cm2/g, for 10 to 30 percent, resulting mortar showed equivalent properties, fluidity and strength, with those using current portland blast-furnace slag cement. Because clinker content in produced mortar is less than that of the currently available cement, use of the newly developed cement could lead to a reduction of cement-originated CO2 gas emission in the concrete sector.