Abstract
This paper discusses the effects of reinforcing steel corrosion on the shear resisting mechanism of RC box culverts and the applicability of the material degradation model in a finite element method. First, in FEM analyses, loss of reinforcement section area and initial tension strain due to reinforcement corrosion, and deteriorated bond characteristics between reinforcement and concrete, were considered. Second, cyclic loading tests using full-scale corroded specimens were numerically analyzed. The analyzed crack patterns and load-displacement relationships up to the maximum load were observed to be in close agreement with the experiment results within the average corrosion ratio of 10% of primary reinforcement. The fact that corrosion cracks can importantly affect the progression of shear cracks and shear strength of RC beams was also found. On the other hand, we established that RC box culverts being statically indeterminate structures, sectional forces are redistributed after cracking damage, and local material deterioration has a minor effect on shear capacity. Furthermore, a parametric study was carried out for corroded RC box culverts using parameters such as size, steel corrosion location, and corrosion level.