Abstract
Quantitative measurement of the texture of copper filaments which were obtained by the glass conjugated melt spinning was performed and the following results were obtained.
A single (001) fiber texture is observed for the copper filament. Quantitative orientation evaluation of the crystallite of the fiber texture is made by the method of the preferred orientation analysis of the crystalline polymers.
The degree of the orientation distribution of fiber axis increased with the increased tensile stress and decreased with the increasing effect of rapid cooling. In addition to these results, the degree decreases along the diameter direction of copper filament.