Abstract
In this paper, the local distribution of austenite grain size (AGS) was experimentally determined by conducting single round-oval and square-diamond pass hot bar rolling experiments of AISI4135 steel. The rolling experiments were carried out using the laboratory mill. The local distribution of AGS was also determined numerically. In order to predict AGS distribution, the AGS evolution model was combined with three dimensional non-isothermal finite element analyses by adopting a modified additivity rule. AGS evolution model was experimentally determined from hot torsion test according to Hodgson's model. The predicted results were in a reasonably good agreement with experimental results.