Influence of Zinc Ions on Initial Stage of Localized Corrosion of Zn and Zn–Al Alloy Coated Steels with Photon Rupture Method
Masatoshi SakairiYoshiyuki UchidaTatsuya KikuchiHideaki Takahashi
Author information
JOURNAL FREE ACCESS

2008 Volume 48 Issue 7 Pages 988-993

Details
Abstract

The effect of pre-dissolved Zn ions in the solutions on the initial stage of localized corrosion after oxide films of Zn and Zn–Al alloy coated steels were removed by a photon rupture method, focused pulsed Nd-YAG laser beam irradiation, was investigated electrochemically. Zn ions can be inhibited dissolution of the Zn coated layer by precipitation of zinc hydroxide, which is formed by hydrolysis reaction of dissolved Zn ions in neutral buffer solutions. However, Zn ions do not affect the dissolution of a Zn–Al alloy coated layer. The absence of inhibition of the Zn–Al layer dissolution can be explained by pH change to lower values at the irradiated area by the hydrolysis reaction of the dissolved Al ions. The effect of Zn ions on corrosion inhibition of the coated layer by the photon rupture method established here was in good agreement with polarization experiments.

Content from these authors
© 2008 by The Iron and Steel Institute of Japan
Previous article Next article
feedback
Top