Interfacial Reaction between Al2O3–SiO2–C Refractory and Al/Ti-Killed Steels
Young Seok LeeSung-Mo JungDong-Joon Min
Author information
JOURNALS OPEN ACCESS FULL-TEXT HTML

2014 Volume 54 Issue 4 Pages 827-835

Details
Abstract

In the current investigation, the thin film method was employed to clarify the formation mechanism of the oxide layers at the interface between the Al2O3–SiO2–C refractory and liquid Fe. A reacted layer was formed in such a way that initially FeO-enriched liquid layers are widely distributed on the Fe surface and FeO and SiO2 in the liquid layer are reduced by Al in liquid Fe to develop solid Al2O3-enriched layer of inclusions. Some inclusions in liquid Fe might be produced by the remaining oxygen in Ar gas being supplied through the nozzle to prevent the adherence of inclusions onto it. The oxide layers at the interface estimated by thermodynamic calculation are in good accordance with the experimental results of the reaction between Al2O3–SiO2–C refractory and Al-killed/Al-Ti-killed steels previously reported.

Information related to the author
© 2014 by The Iron and Steel Institute of Japan
Previous article Next article
feedback
Top