Fundamental Study of Sn Removal from Hot Metal by NH₃ Gas Blowing

Abstract

Development of a practical method of Sn removal in the steelmaking process is necessary from the viewpoints of promoting use of scrap procured in the market and reducing energy consumption. It is well known that Sn promotes surface cracks of billets in hot rolling by coexisting with Cu. Although various methods of Sn removal have been investigated in laboratory experiments, enough Sn removal efficiency for commercially use has not been obtained. In the present study, Sn removal from high-S hot metal by NH₃ gas blowing was investigated in laboratory experiments as a new method of Sn removal. The laboratory experiment on Sn removal from hot metal was carried out using up to a 10 kg-scale vacuum induction melting furnace. Sn removal was accelerated while blowing NH₃ gas, and the evolution of gas bubbles were observed at the hot metal surface. Within the ranges of these experiments, higher temperature and higher concentrations of S and N were advantageous for Sn removal. The mechanism of the acceleration of Sn removal by NH₃ gas blowing could be estimated that oversaturated N or H in hot metal made small bubbles to increase the hot metal surface for SnS evaporation. In the estimation of Sn removal ratio in plant-scale operation, it could reach 40%. For further rapid Sn removal, it was necessary to maximize [N] of hot metal by optimizing the lance height or flow rate of NH₃ gas.