Reaction Mechanism of Ferrosilicon Synthesis Using Waste Plastic as a Reductant
Rifat FarzanaRavindra RajaraoVeena Sahajwalla
Author information
JOURNALS OPEN ACCESS FULL-TEXT HTML

2017 Volume 57 Issue 10 Pages 1780-1787

Details
Abstract

Reaction mechanism study of ferrosilicon synthesis was carried out by using reagent grade material, graphite and waste plastic, Bakelite as reducing agent over a temperature range of 1623 K to 1823 K (1350°C to 1550°C) under inert atmosphere. Reaction rate was determined by using off-gases evolving from reduction reactions. Results showed that reduction mechanism was predominantly controlled by chemical reactions with both the reducing agent. Initially Bakelite bearing pellet showed faster reaction rate compared to graphite due to volatiles generation and less crystalline nature of Bakelite derived carbon. Extent of reduction can be improved by increasing temperature; however Bakelite bearing pellet showed lower dependency on temperature compared to graphite. Activation energy for graphite and Bakelite pellet is 238.07 kJ/mol and 140.29 kJ/mol respectively. This comparative study will create new opportunities to use waste Bakelite as a reductant even at moderately lower temperature to synthesise ferrosilicon alloy.

Information related to the author
© 2017 by The Iron and Steel Institute of Japan
Previous article Next article
feedback
Top