2023 Volume 63 Issue 4 Pages 631-638
Towards better understanding of fundamental dephosphorization slags of the FeO-CaO-SiO2-P2O5 quaternary system, this study aimed at clarifying the thermochemical properties of iron oxide in Ca2SiO4-Ca3P2O8 solid solutions. The solubility and activity of FeO in the solid solutions coexisting with CaSiO3 at 1573 K were determined by SEM-EDX analysis and a gas equilibrium method, respectively. Based on the present experimental results, the phase relationships could be explained that the solid solution of high FeO solubility coexists with CaSiO3 and liquid slag of low FeO content, while the solid solution of low FeO solubility coexists with CaO and liquid slag of high FeO content.