Abstract
In this study, the effects of dilution on the HAZ liquation cracking susceptibility of PTAW (Plasma Transferred Arc Welding) Inconel 625 and Inconel 718 overlay on Nimonic 80A were observed. In order to evaluate the HAZ liquation cracking susceptibility, the Varestraint test was utilized. A possible mechanism of HAZ liquation cracking was suggested, on the basis of microstructure examination and thermal analysis.
The HAZ liquation cracking of the diluted Inconel 625 and Inconel 718 with Nimonic 80A was closely related with solidification temperature range and the amount and distribution of γ/NbC and γ/Laves eutectic phases formed along the solidification grain boundaries. As the dilution was increased, the C/Nb ratio increased, while the amount of eutectic phases decreased. The solidification temperature range was lowered with increases in the dilution in each overlay. Therefore susceptibility of HAZ liquation cracking diminished with increases in dilution.