Measurement of Dynamic Strain Aging in Pearlitic Steels by Tensile Test
Berenice Mendonça GonzalezLeandro Aparecido MarchiEvilmar José da FonsecaPaulo José ModenesiVicente Tadeu Lopes Buono
Author information
JOURNALS FREE ACCESS

2003 Volume 43 Issue 3 Pages 428-432

Details
Abstract

The mechanical behavior of a pearlitic steel was studied by means of tensile tests performed in the temperature interval from 298 to 773 K, at strain rates from 10−4 to 10−2 s−1, aiming to analyze the role of cementite decomposition in the dynamic strain aging (DSA) phenomena occurring in these steels. Typical features of DSA were observed: serrated flow (the Portevin-LeChatelier-PLC effect), the presence of a maximum and a minimum in ultimate tensile strength and reduction of area versus temperature curves, respectively, and a less evident maximum in the yield strength versus temperature curve. Apparent activation energies were calculated based on the onset of the PLC effect, the maximum in ultimate tensile strength and the minimum in reduction of area. Results suggest that changes in mechanical properties associated with DSA in pearlitic steels are related to cementite decomposition. Differences on the phenomenological aspects regarding DSA in pearlitic and in low carbon steels are discussed, based on the kinetics of the process.

Information related to the author
© The Iron and Steel Institute of Japan
Previous article Next article
feedback
Top