Background and Aims: Er:YAG laser has become optional for enamel and dentin preparation for a decade.
However, it is unclear if Er:YAG laser is acceptable for enamel conditioning prior to an application
of a pit-and-fissure sealant. This in vitro study thus aimed to investigate shear bond strength of a sealant to enamel etched with Er:YAG laser, as well as to demonstrate an alteration of enamel surface after the
laser was applied.
Materials and Methods: One hundred and twenty extracted human premolars were divided into 4 groups (N = 30 per group) in which the enamel surfaces were treated with 1) 37% phosphoric acid, 2) Er:YAG laser 80 mJ/pulse, 2 Hz, 3) Er:YAG laser 120 mJ/pulse, 10 Hz, and 4) Er:YAG laser 140 mJ/pulse,
2 Hz. Prior to sealant application. Shear bond strength was determined by using a universal testing machine.
Statistical analysis was performed using One-way ANOVA. Modification of enamel surface after laser ablation was also investigated using scanning electron microscope.
Results: Phosphoric acid-etched enamel yielded the highest shear bond strength when bonded with a sealant. Ablation of enamel with Er:YAG laser did not significantly improve sealant bonding since it demonstrated lower shear bond strength, compared to acid-etched enamel. Despite the presence of cracks after Er:YAG laser application, dissolution of enamel substances was limited.
Conclusion: Our study has shown a reduced shear bond strength of dental sealant to an Er:YAG laser-irradiated enamel, compared with phosphoric acid-etched enamel.