1991 Volume 99 Issue 1153 Pages 793-797
Superconducting thick films 1mm wide and 1-100μm thick were prepared on Ag substrates by gas deposition using a YBa2Cu3O7-x (123) ultrafine powder. After heat treatment at 850°C for 10h in O2 atmosphere, a 123 thick film (1μm) with random grain orientation had a Jc of 2300A/cm2 at 77K. The effects of Ag substrate and the depression of melting point of 123 ultrafine powder were discussed from a thermodynamic point of view.