2020 Volume 128 Issue 2 Pages 80-83
Formation of solid solutions was examined in a wide miscibility gap system of Ba1−xCaxZrO3 by preparing film samples having amorphous structures with the help of rf magnetron sputtering and then annealing the amorphous film samples at a moderate temperature condition. Ba1−xCaxZrO3 solid solutions were successfully formed as monophasic products over the entire Ca composition range, indicating the usefulness of the method for the formation of solid solutions in perovskite-type oxides, and Ca composition dependence of the permittivity was revealed in the solid-solution system.