2023 Volume 58 Issue 3 Pages 108-115
We approached the internal matrix reinforcements using the Cu-Sn-Zn and Cu-Sn-In ternary bronze alloy matrices. After Nb3Sn phase synthesis, these ternary bronze alloy matrices were transformed into(Cu, Zn)or(Cu, In)solid solutions having much higher mechanical strength. Jc degradation due to the transverse compressive stress on the internal matrix reinforced Nb3Sn multifilamentary wire was evaluated. No Jc degradation was observed at approximately 100 and 150 MPa, which values were much higher than the conventional bronze processed Nb3Sn wire. We found that the internal matrix reinforcement was effective for suppressing Jc degradation due to transverse compressive stress.