Non-linear Magnetic Response of RuSr2Gd1.5Ce0.5Cu2O10−δ Superconductor
Yoshihiro UragamiYoshiaki HataHiroshi Yasuoka
Author information
JOURNAL OPEN ACCESS

2006 Volume 53 Issue 9 Pages 701-706

Details
Abstract
We have investigated the magnetic response of superconductivity on the magnetic superconductor RuSr2Gd1.5Ce0.5Cu2O10−δ. The high-quality polycrystalline sample was synthesized with the additional excess ruthenium. Superconductivity of the sample appears below 31 K. Fundamental and higher-harmonic complex susceptibilities χn=χn'−n'' were measured. For all n, χn appears below 26 K. The results suggest the sample magnetizes non-linearly to magnetic fields below the temperature. The magnetization curves at low magnetic fields were obtained by substituting observed χn in Fourier series of the time-dependent magnetization. The magnetization curve below 31 K indicates a hysteresisless diamagnetism. The diamagnetism is due to the intragrain superconductivity. The magnetization curve below 26 K indicates a hysteresis loop as the mixed state in type-II superconductors simultaneously with the hysteresisless diamagnetism. The hysteresis loop is due to the intergranular superconductivity. From the hysteresis width of the magnetization curve, the intergranular-critical current density was estimated at 7.5×103A/m2 on 5 K.
Content from these authors
© 2006 by Japan Society of Powder and Powder Metallurgy

本論文はCC BY-NC-NDライセンスによって許諾されています.ライセンスの内容を知りたい方は,https://creativecommons.org/licenses/by-nc-nd/4.0/deed.jaでご確認ください.
https://creativecommons.org/licenses/by-nc-nd/4.0/deed.ja
Next article
feedback
Top