Rapidly solidified superconductive glass ceramics (Bi:Sr:Ca:Cu=2:2:2:3) was produced by centrifugal atomization of molten oxides. Main product was spherodized glassy powder, while glassy flakes and ligaments were also obtained. The existence of superconductivity above 80K was observed after heat treatment. The state of crystallization was also investigated.