Abstract
The nitrogen content of the aluminum alloys including tin sintered in nitrogen gas was less than 1/10 compared to the sintered material without tin. It is considered that liquid tin covered the surface of aluminum particles and prevented the formation of AIN during sintering. The amount of in-situ formed AIN depended on both the chemical compositions of raw powder and the specific particle surface area and in particular was proportional to the surface area.