Effects of Clear and Amber Cullet on Physical and Mechanical Properties of Glass-Ceramics Containing Zinc Hydrometallurgy Waste

Abstract

The effect of glass cullet on physical and mechanical properties of glass-ceramics developed from zinc hydrometallurgy waste and glass cullet was investigated. The glass-ceramics were prepared by mixing zinc hydrometallurgy waste with glass cullet through vitrification process. Two difference types of glass cullet (clear and amber cullet) were used. The parent glasses were ground and pressed into bars and sintered at low temperature (850°C) for 2 hours. The obtained glass-ceramics had low porosity. The glass-ceramics with clear cullet exhibited higher density and strength, comparing with the glass-ceramics with amber cullet. The type and the amount of the glass cullet present in the glass-ceramics have strong effect on their properties.