2010 Volume 4 Issue 2 Pages 189-195
Currently a new generation of relaunchable space transportation system using liquid hydrogen/ liquid oxygen rocket engines is under development. The inner combustion chamber is exposed to extreme thermal loads and environmental attack during starts. To prevent failure of the cooling channels, a thermal barrier coating to provide thermal and oxidation protection could be applied. Thermal barrier coatings are state of the art for gas turbines and this concept should be transferred to copper substrates in rocket engine applications. The thermomechanical loading conditions are quite different from the gas turbine applications as heat fluxes and temperature gradients are much higher while overall service time is much shorter. As a start for optimization of a suitable coating, a material system known for gas turbines is employed. In this work a thermal barrier coating system is applied by atmospheric plasma spraying to the copper-based high strength alloy Cu-1%Cr-0.3%Zr. The bond coat consists of a NiCrAlY alloy, while partially stabilized zirconia is used as a top coat. Spraying parameter optimization for the new substrate is described. The reached coating system is tested in thermal cycling experiments, where no failure of the coating could be detected. In oxidation experiments good environmental protection of the coating is shown.