Abstract
The long-term integrity of TRU waste package, with a titanium alloy for the outer corrosion resistance layer and carbon steel for the inner structural vessel, has been evaluated.
The target confinement period is settled at 60,000 years in this study (i.e., 10 times of half-life). So the outer corrosion resistance layer with titanium (Ti-Pd alloy) is developed through focus on the high corrosion resistance of Ti alloy as a technology that has long-term confinement.
In investigation about integrity of its passive film, the thickness of corrosion layer of 60,000 years is calculated by building an empirical formula between temperature and corrosion current density, considering the results of constant voltage examination in the TRU waste repository assumed environment. About crevice corrosion, its occurrence conditions is investigated in the TRU waste repository assumed environment, then, Ti.Gr-17 is selected as candidate material of the corrosion resistance layer. In investigation about SCC in Ti alloy, using the models of growth of hydride-layer, the thickness of hydride-layer after 60,000 years is estimated by the results of constant currents tests. Then, the hydride-layer of this thickness is confirmed not to generate cracks, in consideration of destructive critical hydride cracking thickness and the models of crack propagation. The knowledge that the process of generation of hydrogenated layers changes with differences in acceleration conditions (i.e., current density) is obtained. So we must confirm the adequacy of this model by the examination with natural condition.