Hole Distribution in (Sr,Ca,Y,La)₁₄Cu₂₄O₄₁ Compounds Studied by X-ray Absorption and Emission Spectroscopy

Abstract

The polarization dependence of soft x-ray absorption spectroscopy (XAS) and x-ray emission spectroscopy (XES) near the O 1s absorption edge was measured on two-leg ladder single-crystalline samples of (Sr,Ca,Y,La)₁₄Cu₂₄O₄₁ (14-24-41). The hole distributions in 14-24-41 compounds are determined by polarization analysis. For samples with less than or equal to 5 holes/chemical formula (c.f.), all holes reside on the edge-shared chain layer. In the case of Sr_14−xCa_xCu₂₄O₄₁ (6 holes/c.f.), there is approximately one hole on the two-leg ladder layer, with about five holes remaining on the edge-shared chain layer. By Ca substitution for Sr in the Sr_14−xCa_xCu₂₄O₄₁ samples, 0.3 holes transfer from the edge-shared chain to the two-leg ladder layer. It is possible that some of the holes on the two-leg ladder layer move from the rung sites to the leg sites upon Ca substitution.