Abstract
Hardness of Zr-Al-Ni-Cu glass, which alloy is characterized by a smaller critical cooling rate, was measured in the heating process from RT to 773K. Along the increasing temperature up to 673K, the Vickers hardness decreased to one half of that at RT. At higher temperature, crystallization resulted in a drastically increased hardness.