In the present study, fatigue crack propagation behavior and crack closure phenomenon of the aluminum alloy A6061 and carbon steel JIS S25C were investigated in detail. Differences in the crack closure behavior between them were discussed on the viewpoints of the compressive residual stress, the plasticity wake, and the roughness of the fracture surface.