Abstract
The changes in the barrier properties due to the damage imposed on the SiOx deposited nylon 6 films accompanying various deformations such as bending and elongation were examined by evaluating the corrosion rate of the copper plates by H2S kept in the pouches made of the damaged films. After application of elongational deformation of as high as 2% or less, only slight corrosion of the copper plates, almost similar to those of the copper plates kept in the pouches made of undeformed films, was observed. After application of elongational deformations of 3% or more, the corrosion of the copper plates was more distinct and proceeded significantly with time, Bending deformation given to the SiOx deposited nylon films also deteriorated the barrier property to H2S when the radius of curvature at the bent part was small. Comparison of the corrosion rates of the copper plates kept in the pouches made of films deformed in various ways and undeformed commercial films shows a clear relationship between the H2 permeation rate of the films and the corrosion rate of the copper plates by H2S.