X-ray Measurement of Residual Stress on Bolt Threads

Abstract

This study deals with X-ray measurement of residual stress at the local area around the thread root of a bolt. Residual stress in the 0.5 mm×5 mm area was measured using a method of stepped scanning and parabolic approximation. The conditions of measurement had been determined and evaluated through the preliminary measurement of compressive stress acting on the cylindrical surface. Furthermore, the fatigue strength estimated by applying the residual stress data to the previously presented hypothesis was compared with the experimental results. The main conclusions obtained were as follows: (1) The residual stress in a relatively small area on the cylindrdcal surface with large curvature can be measured by X-ray using a method of stepped scanning and parabolic approximation; (2) The compressive residual stress measured at the thread root was larger for the bolt manufactured by thread rolling after heat treatment than for one manufactured by thread rolling before heat treatment; (3) The distribution of residual stress along the axial direction from the thread root to the portion under crest did not represent remarkable change in its value; (4) The residual stress of a bolt was somewhat decreased by fatigue loading on the condition of low mean stress; (5) The fatigue strength estimated using residual stress data showed the tendency of experimental results well.