2014 Volume 38 Issue 3-2 Pages 143-146
We fabricated FeCuPt grains by using a combination of Rapid Thermal Annealing with Rapid Cooling Process. The isolated grains consist of mostly L10-ordered and polycrystalline structure. We carried out additional annealing on these isolated FeCuPt grains to achieve single crystallization of grains. The surface morphology and detailed crystal structure of the grains are observed. After additional annealing, FeCuPt grains retained almost the same grain size. As a result, single crystalline L10-FeCuPt isolated grains were obtained by combining RTA with RCP and by carrying out additional annealing. Furthermore, we characterized the thermo-magnetic properties of single crystalline L10-FeCuPt isolated grains and increased areal grain density by forming additional grains.