1992 Volume 1992 Issue 4 Pages 426-428
A new technique for synthesizing ZnsFe3-xO4powders from α-Fe2O3 and Zn under an argon flow by the thermite method is presented. The ZnxFe3, O4 fine powders (O.3 to O.6μm) of single phase were successfully synthesized at 500 °C for 3 h using the powder mixture of Zn/α-Fe2O3=0.35 (molar ratio). The saturation magnetization and coercive force of the ZnxFe3-xO4 powders were 97 emu/g and O.11 kOe, respectively.