1999 Volume 1999 Issue 6 Pages 369-373
In order to confine hydrogen in hydrogen storage alloys, a new method, i. e. immersion of the alloy into a solution consisting of some kind of oxidants, was examined. Strong confining effect of hydrogen was observed by the immersion of the alloy in the solution containing chromate ion even after the alloy was kept under the atmosphere for more than 5000 hours.
It was shown from results of XPS and AES tha t nickel particles on the alloy surface which act as active sites for hydrogen absorption/desorption were changed into nickel oxide by the confining treatment, and the oxide remained to be stable by residual chromate ion on the alloy surface. By formation of the nickel oxide, i. e., vanishment of surface active sites, it is presumed that hydrogen was confined in the hydrogen storage alloy after the treatment.
In the case of Ni-MH batteries, rem aining capacity of negative electrodes agree well with the capacity evaluated from the amounts of hydrogen in the hydrogen storage alloys (active material for negative electrode) after the treatment.
This article cannot obtain the latest cited-by information.