A novel pnictide-oxide BaTi2Sb2O was synthesized by solid state reaction. XRD revealed that BaTi2Sb2O consists of alternate stacking Ba layers and Ti2Sb2O layers with lattice constants a = 4.111, c = 8.072. This compound shows metallic behavior and an anomaly was observed in electrical resistivity and magnetic susceptibility at around 50 K, as seen in the related compound Na2Ti2As2O, where a SDW/CDW transition was reported.