Measurement of erosion of stainless steel by molten lead-free solder using micro-focus X-ray CT system

Abstract

The severe erosion damage, which is caused by a molten lead-free solder, of wave solder equipment made into stainless steel has been encountered in operation. Then, the higher maintenance frequency and reduced life time of wave solder machine component is a serious issue in a manufacturing process. In this study, the evaluation method of erosion of stainless steel by molten lead-free solders was investigated using micro-focus X-ray systems for fluoroscopic and computed tomography (CT). As a result, it was found that the fluoroscopic image could truly reconstruct the cross-section shape of the stainless steel sample after immersion test without destruction. In the case of X-ray systems for fluoroscopic and CT used in this study, three-dimensional data can be obtained. Therefore, it was possible to easily check the whole picture of the test sample after immersion test and to decide the maximum erosion depth of test sample.