2022 Volume 40 Issue 4 Pages 226-237
Advanced high strength steel sheet (AHSS) is widely used in the automotive body for weight reduction and the improvement of crash performance. Peel tensile strength of spot welds tends to decrease as the steel sheet strength increases. Therefore, in order to further expand the application of AHSS, technology to prevent fracture of spot welds is required. In order to achieve that, it is necessary to understand the characteristics of spot welded joints and clarify the controlling factors. However, most of the conventional joint strength evaluations have been conducted on the same kind material joints, and there are few systematic studies on the joint strength and fracture mode of dissimilar material joints that are often used in actual vehicles. Therefore, the purpose of this study is to obtain a guideline for grasping the characteristics of dissimilar joints in case of the plug failure. Using various joint shapes, we compared the peel tensile strength and failure position of the same kind material joints and the dissimilar material joints with the TS1500MPa class hot stamped steel sheet. As a result, it was found that the deformation behavior of the test piece affects the joint strength and fracture position of the dissimilar material joints. Specifically, in dissimilar material joints, cross tension joints and double cup-shape tension joints tended to break on the TS1500MPa class hot stamped steel side. On the other hand, L-shape tension joints broke on the lower strength material side. From these results, it is considered important to understand their deformation behavior in order to analyze and predict the fracture phenomenon of spot welds in actual vehicles and automotive parts.