Abstract
Copper and aluminum were bonded at 298 K by electrodeposition of copper. The faying surface of the aluminum was anodized to improve the interface strength between the deposited copper and aluminum. Many tubular pores with diameters of several tens of nm were formed in the anodic oxide (alumina) film on the aluminum surface along the film growth direction, and the higher the anodic oxidation voltage, the larger the pore diameter and the thicker the wall between the pores. Electrodeposited copper and aluminum were bonded through the porous oxide film, forming a bonding interface where copper was electrodeposited in the pores in the oxide film. Although the joint was made through the oxide film at the bonding interface, it was found that there was electrical conductivity between the copper and aluminum. No intermetallic compounds were observed at the interface between the electrodeposited copper and aluminum. Electrodeposited copper in the tubular pores in the oxide film on the aluminum surface caused an anchoring effect at the joint interface, resulting in a sound joint with base metal fracture on the aluminum side.