1965 Volume 34 Issue 6 Pages 572-578
Using the same method as 1 st report, the authors calculated carbon equivalents for mechanical properties of high strength basic weld deposit treated stress relief annealing.
Further the authors searched for the equations between carbon equivalent and the values of mechanical properties of weld deposits.
The results obtained in the study are follows:
CeqS.R(Y.P)=C+0.08 Si+0.10 Mn+0.04 Ni+0.12 Cr+0.25 Mo
CeqS.R(T.S)=C+0.09 Si+0.06 Mn+0.03 Ni+0.09 Cr+0.17 Mo
CeqS.R(EL)=C+0.14 Si+0.11 Mn+0.03 Ni+0.16 Cr+0.14 Mo
CeqS.R(E0)=C+0.27 Si+0.07 Mn+0.05 Ni+0.19 Cr+0.20 Mo
CeqS.R(E-40)=C+0.38 Si+0.09 Mn+0.05 Ni+0.23 Cr+0.20 Mo
Y.P (kg/mm2)=29.2+80.2 CeqS.R(Y.P)
T.S (kg/mm2)=26.4+147 CeqS.R(T.T)
EL (%)=37.1-29.1 CeqS.R(EL)
E0 (kg-m/cm2)=48.1-69.2CeqS.R(E0)
E-40 (kg-m/cm2)=28.7-37.4 CeqS.R(E-40)