1978 Volume 47 Issue 8 Pages 514-518
Effects of the mottled appearance on the high temperature ductility was investigated. Longitudinal all-weld-metal specimens of as welded and annealed conditions with different levels of contrast were prepeared. The results may be summalized as follows.
1. Progressive increase in the contrast produced a marked decrease in high temperature ductility.
2. The decrease in ductility was observed for both specimens of as welded and annealed conditions. The results obtained seem to suggest a ceartain relation between the mottled appearance and the less ductility.