In the process of etching aluminum electrolytic capacitors, high purity (99.99%) aluminum was galvanostatically electrolyzed at a current of-800mA/cm2 for 20s in a 1.0%NaCl solution containing HCl and alumina powders, and pitting sites were produced at a density of 1.4×1012/m2on the surface.