2020 Volume 72 Issue 11 Pages 433-443
Iron compounds contained in typical Al2O3-SiO2 refractories were investigated by cross-section observation, micro spot composition analysis and micro spot X-ray diffraction. The morphology of iron compounds could be classified adjacent with pores system (type-A) and included in the aggregates system (type-B). And the point of iron compounds in type-A was an aggregate composed of many particles. Fe2O3 and/or TiO2 were dispersed in the aggregate in type-B. The particles of iron compounds in type-A were identified as hematite. However, in the 1400 ℃(0.5h)-fired sample, the particles were identified as rutile and mullite. The Fe-components might have diffused after high temperature heat treatment.