2005 Volume 2005 Issue 220 Pages 280-282
The deposition behavior of metal particles with the carbonization of Sugi wood containing metal salts, such as Cu (NO3) 2 and NiCl2, was studied as the first step of the research in the present work for preparing charcoals with a high thermal conductivity. Sugi wood containing these metal salts was carbonized in an argon gas for 1h at the temperature range from 400 to 1000°C. The charcoals dispersed with metal particles were thus obtained above 400°C. From FE-SEM observations of the obtained charcoals with metal particle, the deposition behavior of Ni particles was found to be different from that of Cu particles.