Abstract
Mesophase-pitch-based carbon fiber P 100 is known as a well-oriented carbon fiber in which the partially graphitized crystallites align along the fiber axis. The X-ray powder diffraction pattern for P 100 measured by the X-ray diffractometer reveals the 100 diffraction line as a composite peak with the 101 diffraction line. The composite peak is usually not easy to separate into the component peaks of 100 and 101 lines. In the present article, a method to measure the single 100 diffraction line with the X-ray diffractometer using fiber samples of P100 has been developed. It has been found that there exist two types of crystallites oriented to their basal planes along the fiber axis in each of the P 100 fibers; the Z-type crystallite with the zigzag boundary planes and the A-type crystallite with the armchair boundary planes, both of the boundary planes are perpendicular to the fiber axis. The average crystallite sizes along the fiber axis evaluated are 53 nm for the Z-type crystallites and 80 nm for the armchair crystallites. The average crystallite thickness for both types is about 120 nm.