Reaction Mechanism between Solid CaO and FeOx-CaO-SiO2?P2O5 Slag at 1573K
Tasuku HAMANOShinya FUKAGAIFumitaka TSUKIHASHI
Author information
JOURNALS FREE ACCESS

2006 Volume 92 Issue 11 Pages 649-654

Details
Abstract

Solid CaO and FeOx-CaO-SiO2-P2O5 slag were reacted for 2 to 2400 s at 1573K. The interface of CaO and slag was observed and analyzed by SEM/EDS. The CaO-FeO layer was formed beside solid CaO. The thickness of the CaO-FeO layer increased with time. Next to the CaO-FeO layer, 2CaO·SiO2 phase was formed in the melt and high content of FeO was included in the liquid. The activities of FeO and CaO for each phase were evaluated and reaction mechanism between solid CaO and FeOx-CaO-SiO2-P2O5 slag was discussed. The activity of FeO for 2CaO·SiO2 saturated melt is larger than that for the CaO-FeO layer, therefore, Fe2+ diffuses from slag phase to solid CaO. Then the CaO-FeO layer is formed beside solid CaO. The pass of the slag composition change accompanied by CaO dissolution are represented in the phase diagram for the FeOx-CaO-(SiO2+P2O5) pseudo ternary system.

Information related to the author
© The Iron and Steel Institute of Japan
Previous article Next article
feedback
Top