Abstract
KNO3 nano-particles with the diameter of about 28 nm were prepared by mechanical milling using planetary ball mill from the commercial KNO3 powder. Rotation speeds of ball mill were 0 to 500 rpm, where the milling time was kept at 15 minutes. Magnetization was measured by SQUID magnetometer. The milled sample at 500 rpm showed same order of saturation magnetization as that of BaTiO3 with vacancies.
