2016 Volume 41 Issue 3 Pages 289-295
Raman measurements and uncertainty evaluations were conducted for C60 fullerene nanowhiskers (C60FNWs) synthesized using the liquid-liquid interfacial precipitation (LLIP) method and for a vacuum-deposited C60 thin film. No photopolymerization was observed for the C60 molecules when the specimens were irradiated by a green laser of 532 nm wavelength at a power density of 5.7×103 mW/mm2. It is demonstrated that the 1469.95 ± 0.42 cm-1 can be used as a standard peak position of the Ag(2) mode of C60FNWs.