The authors have already established a new
CTOD calculation formula, and have been revised a
CTOD testing standard of WES1108 in the Japanese Welding Engineering Society by using this formula. Because the fatigue pre-crack tip should be placed in the specified microstructure such as HAZ for the critical
CTOD evaluation of welded joints, the next step is the application of the formula to various crack length-to-width ratio,
a0/
W, conditions, especially for shallow crack specimens. In the previous work, a rotational deformation was apparently observed, and the plastic rotational factor,
rp, was described as a function of wide
a0/
W range. However, a simple use of
rp did not result in a better
CTOD estimation for shallow crack specimens.
In the present work, another way of calculating
CTOD was developed by the numerical investigation of single edge notch bend, SE(B), specimens with various
a0/
W. Non-linear crack opening profiles were dominant for smaller
a0/
W specimens than 0.2 due to plastic deformation behind their crack tips, or a straight crack opening profile deviated from a triangle side assumed by the plastic hinge model for
a0/
W =0.7. In this paper, a correction factor of the plastic component of clip gauge displacement,
CVp, was proposed considering non-linear crack opening and crack profile deviation, and it was demonstrated that
CVp gave a better
CTOD estimation than current
CTOD formulae such as BS7448 and ASTM E1820 for the wide range of
a0/
W.