2019 Volume 87 Issue 1 Pages 52-58
Electrochemical properties of lithium air battery (LAB) cells incorporating highly ordered mesoporous carbon replica (CR) support materials were examined in nonaqueous electrolyte solution of 1 mol/l LiTFSA/TEGDME. The CR support was prepared with pore sizes of 10, 40, and 100 nm. The cycle properties of the LAB cells with the CR support was improved by using Pt-Ru electroctalyst. As a result, the LAB cells with Pt-Ru electrocatalyst/CR (pore size: 10 nm) exhibited the highest performance of the first discharge capacity of 1000 mAh/g and capacity retention of about 50% at 10th cycle. Moreover, different growth behavior of the discharge product was observed as a consequence of the pore size of the CR support.