ゴム/亜鉛めっき鋼直接加硫接着系の環境安定性
2007 年 80 巻 9 号 p. 325-330
詳細
2007 年 80 巻 9 号 p. 325-330
The adhesion stability of rubber/galvanized-steel direct bonding system was studied under several environmental conditions. Following results were obtained. (1) Aging between plates of press machine heated with steam accelerates the degradation of adhesion about 10 times compared with that in oven at the same temperature. (2) Aging under relative humidity 95% or hot water immersion accelerates about 18 times compared with press machine plates aging at the same temperature. (3) Neither ozone aging nor weather meter degradation accelerates so much as high humidity or hot water immersion. (4) The depth of rubber deterioration was 8mm by high pressure oxygen test, 3-4mm by high humidity test or hot water immersion test, and 2mm by hot oven test. (5) The activation energy calculated from the data obtained by press machine plate aging was 107kJ/mol.