2009 年 47 巻 4 号 p. 229-235
Crack Growth Behavior and Redistribution of Residual Stress Caused by Crack Propagation from Residual Tensile Stress Field through Residual Compressive Stress Field of stress corrosion cracking (SCC) and Fatigue. At the beginning, re-distribution of Residual Stress Field boiled and depended on crack propagation was clarified. Based on analysis output, the crack propagation examination check by fatigue test was done. Comparison analyses of analysis output and a fatigue testing result were performed, and consideration was added.